PBT 420SE0
SABIC沙伯基础创新塑料PBT Valox 420SE0性表参数
以下是SABIC沙伯基础创新塑料PBT Valox 420SE0的中英文物性表
SABIC Innovative Plastics Valox® 420SE0 PBT
The property table is provided by www.cn-plas.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.63 g/cc
0.0589 lb/in³
ISO 1183
Moisture Absorption at Equilibrium吸湿平衡
0.070 %
0.070 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation饱和水吸取率
0.090 %
@Temperature 23.0 °C
0.090 %
@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动
0.0010 - 0.0050 cm/cm
0.0010 - 0.0050 in/in
on tensile bar; SABIC Method
 
0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
0.0050 - 0.0070 in/in
@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse线性收缩率/横向
0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on tensile bar; SABIC Method
 
0.0050 - 0.010 cm/cm
@Thickness 3.20 mm
0.0050 - 0.010 in/in
@Thickness 0.126 in
SABIC Method
Melt Flow熔体流动速率
29 g/10 min
@Load 5.00 kg,
Temperature 250 °C
29 g/10 min
@Load 11.0 lb,
Temperature 482 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
 
42 g/10 min
@Load 5.00 kg,
Temperature 250 °C
42 g/10 min
@Load 11.0 lb,
Temperature 482 °F
ASTM D 1238
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Hardness, Rockwell R罗氏硬度
119
119
ASTM D 785
 
119
119
ISO 2039-2
Hardness,硬度 H358/30 
118 MPa
17100 psi
ISO 2039-1
Tensile Strength at Break断裂拉伸强度
120 MPa
17400 psi
Type I, 5 mm/min; ASTM D 638
 
120 MPa
17400 psi
5 mm/min; ISO 527
Tensile Strength, Yield屈服拉伸强度
120 MPa
17400 psi
Type I, 5 mm/min; ASTM D 638
 
120 MPa
17400 psi
5 mm/min; ISO 527
Elongation at Break断裂伸长率
1.9 %
1.9 %
5 mm/min; ISO 527
 
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield屈服伸长率
1.9 %
1.9 %
5 mm/min; ISO 527
 
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus拉伸模量
10.0 GPa
1450 ksi
1 mm/min; ISO 527
 
12.0 GPa
1740 ksi
5 mm/min; ASTM D 638
Flexural Strength弯曲强度
180 MPa
26100 psi
ISO 178
 
186 MPa
27000 psi
brk, 1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus弯曲弹性模量
9.50 GPa
1380 ksi
2 mm/min; ISO 178
 
9.80 GPa
1420 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched悬臂梁缺口冲击强度
0.570 J/cm
@Temperature -30.0 °C
1.07 ft-lb/in
@Temperature -22.0 °F
ASTM D 256
 
0.600 J/cm
@Temperature 23.0 °C
1.12 ft-lb/in
@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched悬臂梁无缺口冲击强度
6.20 J/cm
@Temperature 23.0 °C
11.6 ft-lb/in
@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO) 
6.00 kJ/m²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1A
 
7.00 kJ/m²
@Temperature 23.0 °C
3.33 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO) 
45.0 kJ/m²
@Temperature 23.0 °C
21.4 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1U
 
45.0 kJ/m²
@Temperature -30.0 °C
21.4 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击
5.00 J/cm²
@Temperature 23.0 °C
23.8 ft-lb/in²
@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
 
5.00 J/cm²
@Temperature -30.0 °C
23.8 ft-lb/in²
@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy ImPAct, Notched夏比缺口冲击
0.600 J/cm²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
 
0.700 J/cm²
@Temperature 23.0 °C
3.33 ft-lb/in²
@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test冲击试验数据
5.00 J
@Temperature 23.0 °C
3.69 ft-lb
@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
22
@Load 1.00 kg
22
@Load 2.20 lb
CS-17; SABIC Method
Electrical Properties电性能
Metric公制数据
English英制数据
Comments测试方法
Volume ResiSTivity体积电阻率
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
 
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance表面电阻
>= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant介电常数
3.3
@Frequency 1.00e+6 Hz
3.3
@Frequency 1.00e+6 Hz
IEC 60250
 
3.3
@Frequency 50.0 - 60.0 Hz
3.3
@Frequency 50.0 - 60.0 Hz
IEC 60250
 
3.7
@Frequency 1.00e+6 Hz
3.7
@Frequency 1.00e+6 Hz
ASTM D 150
 
3.8
@Frequency 100 Hz
3.8
@Frequency 100 Hz
IEC 60250
 
3.8
@Frequency 100 Hz
3.8
@Frequency 100 Hz
ASTM D 150
Dielectric Strength介电强度
16.0 kV/mm
@Thickness 3.20 mm
406 kV/in
@Thickness 0.126 in
in oil; IEC 60243-1
 
19.0 kV/mm
@Thickness 3.20 mm
483 kV/in
@Thickness 0.126 in
in air; ASTM D 149
 
22.0 kV/mm
@Thickness 1.60 mm
559 kV/in
@Thickness 0.0630 in
in oil; IEC 60243-1
 
23.0 kV/mm
@Thickness 0.800 mm
584 kV/in
@Thickness 0.0315 in
in oil; IEC 60243-1
 
24.0 kV/mm
@Thickness 1.60 mm
610 kV/in
@Thickness 0.0630 in
in oil; ASTM D 149
Dissipation Factor耗散因数
0.0010
@Frequency 50.0 - 60.0 Hz
0.0010
@Frequency 50.0 - 60.0 Hz
IEC 60250
 
0.0020
@Frequency 100 Hz
0.0020
@Frequency 100 Hz
IEC 60250
 
0.0020
@Frequency 100 Hz
0.0020
@Frequency 100 Hz
ASTM D 150
 
0.010
@Frequency 1.00e+6 Hz
0.010
@Frequency 1.00e+6 Hz
IEC 60250
 
0.020
@Frequency 1.00e+6 Hz
0.020
@Frequency 1.00e+6 Hz
ASTM D 150
Arc Resistance 耐电弧性
60 - 120 sec
60 - 120 sec
Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index相对漏电起痕指数
>= 125 V
>= 125 V
IEC 60112
 
175 V
175 V
IEC 60112
 
175 - 250 V
175 - 250 V
PLC code 3; UL 746A
Hot Wire Ignition, HWI热线圈点燃测试
30 - 60 sec
30 - 60 sec
PLC code 2; UL 746A
High Amp Arc Ignition, HAI高电流电弧点燃测试
>= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
High Voltage Arc-Tracking Rate, HVTR高压电弧跟踪速度
>= 150 mm/min
>= 5.91 in/min
PLC code 4; UL 746A
Thermal Properties热性能
Metric公制数据
English英制数据
Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数
25.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
13.9 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
 
25.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
13.9 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
 
25.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
13.9 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow线性热膨胀系数/横向
89.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
49.4 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
 
89.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
49.4 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
 
120 µm/m-°C
@Temperature 23.0 - 80.0 °C
66.7 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity导热系数
0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at热变形温度 0.46 MPa (66 psi) 
220 °C
428 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
 
212 °C
@Thickness 3.20 mm
414 °F
@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at热变形温度 1.8 MPa (264 psi) 
195 °C
383 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
 
200 °C
392 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
 
200 °C
@Thickness 3.20 mm
392 °F
@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point维卡软化点
200 °C
392 °F
Rate B/50; ASTM D 1525
 
200 °C
392 °F
Rate B/50; ISO 306
 
200 °C
392 °F
Rate B/120; ISO 306
 
220 °C
428 °F
Rate A/50; ISO 306
UL RTI, Electrical相对温度指数
130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact机械冲击热指数
130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数
140 °C
284 °F
UL 746B
Flammability, UL94阻燃等级
V-2
@Thickness 0.400 mm
V-2
@Thickness 0.0157 in
UL 94
 
V-0
@Thickness 0.710 mm
V-0
@Thickness 0.0280 in
UL 94
 
5VA
@Thickness 2.00 mm
5VA
@Thickness 0.0787 in
UL 94
Oxygen Index氧指数
32 %
32 %
LOI; ISO 4589
Glow Wire Test灼热丝试验
960 °C
@Thickness 1.00 mm
1760 °F
@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12