SABIC沙伯基础创新Lexan PC OQ3120物性表参数
SABIC沙伯基础创新Lexan PC OQ3120,并且提供物性表及SABIC企业(原GE)的各种bet官网365入口物性表
PC OQ3120
SABIC沙伯基础创新Lexan PC OQ3120物性表参数
以下是SABIC沙伯基础创新Lexan PC OQ3120中英文物性表资料
SABIC Lexan® OQ3120(bet官网365入口-聚碳酸酯-PC塑料)
The property table is provided by www.cn-plas.com, welcome to download, reprint please indicate the source!
Material Notes:
High Flow. UV-stabilized. Inherent mold release. Ophthalmic lenses.
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium吸湿平衡
0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation吸水率
0.35 %
@Temperature 23.0 °C
0.35 %
@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动
0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow熔体流动速率
26 g/10 min
@Load 1.20 kg,
Temperature 300 °C
26 g/10 min
@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties力学性能力学性能
Metric公制数据
English英制数据
Comments测试方法
Hardness, 硬度H358/30 
95.0 MPa
13800 psi
ISO 2039-1
Tensile Strength at Break断裂拉伸强度
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield屈服拉伸强度
63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break断裂伸长率
70 %
70 %
50 mm/min; ISO 527
Elongation at Yield屈服伸长率
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus拉伸模量
2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength弯曲屈服强度
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus弯曲弹性模量
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO) 
12.0 kJ/m²
@Temperature -30.0 °C
5.71 ft-lb/in²
@Temperature -22.0 °F
80*10*3; ISO 180/1A
 
70.0 kJ/m²
@Temperature 23.0 °C
33.3 ft-lb/in²
@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO) 
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
80*10*3; ISO 180/1U
 
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
 
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击
1.40 J/cm²
@Temperature -30.0 °C
6.66 ft-lb/in²
@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
 
7.30 J/cm²
@Temperature 23.0 °C
34.7 ft-lb/in²
@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
10
@Load 1.00 kg
10
@Load 2.20 lb
CS-17; SABIC Method
Electrical Properties电性能
Metric公制数据
English英制数据
Comments测试方法
Volume ResiSTivity体积电阻率
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance表面电阻
>= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant介电常数  
2.7
@Frequency 1.00e+6 Hz
2.7
@Frequency 1.00e+6 Hz
IEC 60250
 
2.7
@Frequency 50.0 - 60.0 Hz
2.7
@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength介电强度
17.0 kV/mm
@Thickness 3.20 mm
432 kV/in
@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor耗散因数
0.0010
@Frequency 50.0 - 60.0 Hz
0.0010
@Frequency 50.0 - 60.0 Hz
IEC 60250
 
0.010
@Frequency 1.00e+6 Hz
0.010
@Frequency 1.00e+6 Hz
IEC 60250
Thermal Properties热性能
Metric公制数据
English英制数据
Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数
70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity导热系数
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at热变形温度 0.46 MPa (66 psi) 
133 °C
271 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at热变形温度 1.8 MPa (264 psi) 
121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point维卡软化点
139 °C
282 °F
Rate B/50; ISO 306
 
140 °C
284 °F
Rate B/120; ISO 306
 
145 °C
293 °F
Rate A/50; ISO 306
UL RTI, Electrical相对温度指数
80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact机械冲击热指数
80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数
80.0 °C
176 °F
UL 746B
Flammability, UL94阻燃等级阻燃等级
V-2
@Thickness 1.00 mm
V-2
@Thickness 0.0394 in
UL 94
Oxygen Index氧指数
25 %
25 %
LOI; ISO 4589
Glow Wire Test灼热丝测试
850 °C
@Thickness 1.00 mm
1560 °F
@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties光学性质
Metric公制数据
English英制数据
Comments测试方法
ReFRactive Index折射率
1.586
1.586
ISO 489
Haze雾度
<= 0.80 %
@Thickness 2.54 mm
<= 0.80 %
@Thickness 0.100 in
ASTM D 1003
TRansmission, Visible透光率
88 - 90 %
@Thickness 2.54 mm
88 - 90 %
@Thickness 0.100 in
ASTM D 1003