SABIC沙伯基础创新Lexan PC EXL1132T物性表参数
SABIC沙伯基础创新Lexan PC EXL1132T,提供SABIC企业的各种bet官网365入口物性表。
PC EXL1132T
SABIC沙伯基础创新Lexan PC EXL1132T物性表参数
以下是SABIC沙伯基础创新Lexan PC EXL1132T中英文物性表资料
SABIC Lexan® EXL1132T(耐低温塑料-聚碳酸酯-PC塑料)
The property table is provided by www.cn-plas.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Specific Gravity比重 
1.19 g/cc
1.19 g/cc
ASTM D 792
Density密度 
1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption at Equilibrium吸湿平衡 
0.090 %
0.090 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation吸水率 
0.12 %
@Temperature 23.0 °C
0.12 %
@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动 
0.0040 - 0.0080 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0080 in/in
@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse线性收缩率/横向 
0.0040 - 0.0080 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0080 in/in
@Thickness 0.126 in
SABIC Method
Melt Flow熔体流动速率 
19 g/10 min
@Load 1.20 kg,
Temperature 300 °C
19 g/10 min
@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
 
20 g/10 min
@Load 1.20 kg,
Temperature 300 °C
20 g/10 min
@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties力学性能
Metric公制数据
English英制数据
Comments测试方法
Hardness,硬度 Rockwell L 
89
89
ISO 2039-2
Tensile Strength at Break断裂拉伸强度 
56.0 MPa
8120 psi
50 mm/min; ISO 527
 
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield屈服拉伸强度 
57.0 MPa
8270 psi
50 mm/min; ISO 527
 
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break断裂伸长率 
117.9 %
117.9 %
Type I, 50 mm/min; ASTM D 638
 
119.4 %
119.4 %
50 mm/min; ISO 527
Elongation at Yield屈服伸长率 
5.4 %
5.4 %
50 mm/min; ISO 527
 
5.7 %
5.7 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus拉伸模量 
2.26 GPa
328 ksi
50 mm/min; ASTM D 638
 
2.34 GPa
339 ksi
1 mm/min; ISO 527
Flexural Yield Strength弯曲屈服强度 
89.0 MPa
12900 psi
2 mm/min; ISO 178
 
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus弯曲弹性模量 
2.14 GPa
310 ksi
2 mm/min; ISO 178
 
2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched悬臂梁缺口冲击强度
6.18 J/cm
@Temperature -30.0 °C
11.6 ft-lb/in
@Temperature -22.0 °F
ASTM D 256
 
7.36 J/cm
@Temperature 23.0 °C
13.8 ft-lb/in
@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched悬臂梁缺口冲击强度(ISO) 
40.0 kJ/m²
@Temperature -30.0 °C
19.0 ft-lb/in²
@Temperature -22.0 °F
80*10*3; ISO 180/1A
 
55.0 kJ/m²
@Temperature 23.0 °C
26.2 ft-lb/in²
@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)  
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
80*10*3; ISO 180/1U
 
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击  
NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
 
NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击 
4.50 J/cm²
@Temperature -30.0 °C
21.4 ft-lb/in²
@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
 
6.50 J/cm²
@Temperature 23.0 °C
30.9 ft-lb/in²
@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test冲击试验数据 
74.0 J
@Temperature 23.0 °C
54.6 ft-lb
@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Electrical Properties电性能
Metric公制数据
English英制数据
Comments测试方法
Volume Resistivity体积电阻率 
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Surface Resistance表面电阻 
>= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D 257
Thermal Properties热性能
Metric公制数据
English英制数据
Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数 
74.8 µm/m-°C
@Temperature -40.0 - 95.0 °C
41.6 µin/in-°F
@Temperature -40.0 - 203 °F
ASTM E 831
 
74.8 µm/m-°C
@Temperature 23.0 - 80.0 °C
41.6 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow线性热膨胀系数/横向 
76.4 µm/m-°C
@Temperature -40.0 - 95.0 °C
42.4 µin/in-°F
@Temperature -40.0 - 203 °F
ASTM E 831
 
76.4 µm/m-°C
@Temperature 23.0 - 80.0 °C
42.4 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at热变形温度 1.8 MPa (264 psi) 
116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
 
121 °C
@Thickness 3.20 mm
250 °F
@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point维卡软化点 
138 °C
280 °F
Rate A/50; ASTM D 1525
 
138 °C
280 °F
Rate B/50; ISO 306
 
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical相对温度指数 
130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数 
130 °C
266 °F
UL 746B
Flammability, UL94阻燃等级 
HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
UL 94
Glow Wire Test灼热丝测试 
850 °C
@Thickness 0.800 mm
1560 °F
@Thickness 0.0315 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
 
850 °C
@Thickness 3.00 mm
1560 °F
@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
 
960 °C
@Thickness 3.00 mm
1760 °F
@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties光学性质
Metric公制数据
English英制数据
Comments测试方法
Haze雾度 
3.0 %
@Thickness 2.54 mm
3.0 %
@Thickness 0.100 in
ASTM D 1003
Transmission, Visible透光率 
82 %
@Thickness 2.54 mm
82 %
@Thickness 0.100 in
ASTM D 1003