PPO(聚苯醚)GFN3F/沙伯基础(Noryl)物性表参数

责任编辑:文和林发表时间:2020-10-29
沙伯基础(SABIC)Noryl PPO GFN3F是一种加30%玻璃纤维增强PPE + PS混合(聚苯醚),符合FDA规定(适用限制),这种改性聚苯醚树脂低吸水率,水解稳定性,尺寸稳定性,适用于流体工程应用,包括泵壳、叶轮、阀门部件等。
PPO GFN3F
以下是PPO(聚苯醚)GFN3F/沙伯基础(Noryl)物性表参数
PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
FLAME CHARACTERISTICS 1)      
UL Yellow Card Link   E121562-221162 - -
UL Recognized, 94HB Flame Class Rating   ≥1.5 mm UL 94
UV-light, water exposure/immersion   F1 - UL 746C
Oxygen Index (LOI)   26 % ASTM D 2863
MECHANICAL        
Tensile Stress, brk, Type I, 5 mm/min   116 MPa ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min   2 % ASTM D 638
Tensile Modulus, 5 mm/min   9150 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span   180 MPa ASTM D 790
Flexural Stress, yld, 2.6 mm/min, 100 mm span   162 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span   8000 MPa ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span   7170 MPa ASTM D 790
Hardness, Rockwell L   108 - ASTM D 785
Tensile Stress, break   117 MPa ISO 527
Tensile Strain, break   1.8 % ISO 527
Tensile Modulus, 1 mm/min   8500 MPa ISO 527
Flexural Stress   183 MPa ISO 178
Flexural Modulus   8710 MPa ISO 178
IMPACT        
Izod Impact, unnotched, 23°C   588 J/m ASTM D 4812
Izod Impact, notched, 23°C   117 J/m ASTM D 256
Izod Impact, notched, -30°C   124 J/m ASTM D 256
Izod Impact, unnotched 80*10*4 +23°C   31 kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C   35 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C   12 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C   11 kJ/m² ISO 180/1A
Charpy Impact, notched, 23°C   12 kJ/m² ISO 179/2C
Charpy Impact, notched, -30°C   11 kJ/m² ISO 179/2C
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm   39 kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm   47 kJ/m² ISO 179/1eU
THERMAL        
HDT, 0.45 MPa, 3.2 mm, unannealed   142 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed   137 °C ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed   158 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed   137 °C ASTM D 648
CTE, -40°C to 40°C, flow   3.06E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow   6.18E-05 1/°C ASTM E 831
Vicat Softening Temp, Rate B/50   143 °C ISO 306
Vicat Softening Temp, Rate B/120   147 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm   143 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm   137 °C ISO 75/Af
Relative Temp Index, Elec 1) 90 °C UL 746B
Relative Temp Index, Mech w/impact 1) 90 °C UL 746B
Relative Temp Index, Mech w/o impact 1) 90 °C UL 746B
PHYSICAL        
Specific Gravity   1.29 - ASTM D 792
Water Absorption, (23°C/24hrs)   0.06 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm   0.1-0.4 % SABIC method
Melt Flow Rate, 300°C/5.0 kgf   8.7 g/10 min ASTM D 1238
Melt Volume Rate, MVR at 300°C/5.0 kg   7 cm³/10 min ISO 1133
ELECTRICAL        
Dielectric Strength, in oil, 3.2 mm   21.7 kV/mm ASTM D 149
Relative Permittivity, 50/60 Hz   2.93 - ASTM D 150
Dissipation Factor, 50/60 Hz   0.0009 - ASTM D 150
High Voltage Arc Track Rate {PLC}   3 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC}   4 PLC Code UL 746A
High Amp Arc Ignition (HAI), PLC 4   ≥1.5 mm UL 746A
Hot-Wire Ignition (HWI), PLC 1   ≥6 mm UL 746A
Hot-Wire Ignition (HWI), PLC 4   ≥3 mm UL 746A
Hot-Wire Ignition (HWI), PLC 5   ≥1.5 mm UL 746A
Arc Resistance, Tungsten {PLC}   7 PLC Code ASTM D 495
Injection Molding        
Drying Temperature   110-120 °C  
Drying Time   3-4 hrs  
Drying Time (Cumulative)   8 hrs  
Maximum Moisture Content   0.02 %  
Melt Temperature   300-325 °C  
Nozzle Temperature   300-325 °C  
Front - Zone 3 Temperature   290-325 °C  
Middle - Zone 2 Temperature   275-320 °C  
Rear - Zone 1 Temperature   265-315 °C  
Mold Temperature   80-110 °C  
Back Pressure   0.3-0.7 MPa  
Screw Speed   20-100 rpm  
Shot to Cylinder Size   30-70 %
想更多的了解PPO(聚苯醚)GFN3F/沙伯基础(Noryl)物性表参数,请点击以下PDF文档下载:
PPO(聚苯醚)GFN3F/沙伯基础(Noryl)物性表参数
温馨提示:
本物性表参数提供者不承担任何法律责任,建议在选择材料前,就数据值与塑胶材料厂商进行验证。版权归原编辑所有,如有侵权请马上与大家联系.