责任编辑:文和林发表时间:2020-10-29
沙伯基础(SABIC)Noryl PPO GFN30是一种加30%玻璃纤维增强PPE + PS混合(聚苯醚),这种改性聚苯醚树脂低吸水率,水解稳定性,尺寸稳定性,适用于流体工程应用,包括泵壳、叶轮、阀门部件等。
PPO GFN30
以下是PPO(聚苯醚)GFN30/沙伯基础(Noryl)物性表参数
PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
FLAME CHARACTERISTICS 1)      
UL Yellow Card Link   E207780-228546 - -
UL Yellow Card Link 2   E45587-237022 - -
UL Recognized, 94HB Flame Class Rating   ≥1.5 mm UL 94
UV-light, water exposure/immersion   F2 - UL 746C
MECHANICAL        
Tensile Stress, brk, Type I, 50 mm/min   130 MPa ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min   3 % ASTM D 638
Tensile Modulus, 5 mm/min   8600 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span   160 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span   7200 MPa ASTM D 790
Tensile Stress, break, 50 mm/min   110 MPa ISO 527
Tensile Strain, break, 50 mm/min   2.5 % ISO 527
Tensile Modulus, 1 mm/min   8200 MPa ISO 527
Flexural Stress, yield, 2 mm/min   160 MPa ISO 178
Flexural Modulus, 2 mm/min   6800 MPa ISO 178
IMPACT        
Izod Impact, unnotched, 23°C   590 J/m ASTM D 4812
Izod Impact, notched, 23°C   100 J/m ASTM D 256
Izod Impact, notched, -30°C   120 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C   20 J ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C   30 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C   11 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C   10 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm   8 kJ/m² ISO 179/1eA
THERMAL        
Vicat Softening Temp, Rate B/50   147 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed   147 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed   139 °C ASTM D 648
CTE, -40°C to 40°C, flow   2.1E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow   7.5E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow   2.3E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow   7.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50   147 °C ISO 306
Vicat Softening Temp, Rate B/120   149 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm   139 °C ISO 75/Af
Relative Temp Index, Elec 1) 90 °C UL 746B
Relative Temp Index, Mech w/impact 1) 90 °C UL 746B
Relative Temp Index, Mech w/o impact 1) 90 °C UL 746B
PHYSICAL        
Specific Gravity   1.31 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm   0.1-0.4 % SABIC method
Melt Flow Rate, 280°C/5.0 kgf   3.2 g/10 min ASTM D 1238
Water Absorption, (23°C/saturated)   0.1 % ISO 62-1
Moisture Absorption (23°C / 50% RH)   0.04 % ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg   2 cm³/10 min ISO 1133
ELECTRICAL        
Comparative Tracking Index (UL) {PLC}   4 PLC Code UL 746A
High Amp Arc Ignition (HAI), PLC 4   ≥1.5 mm UL 746A
Hot-Wire Ignition (HWI), PLC 0   ≥1.5 mm UL 746A
High Voltage Arc Track Rate {PLC}   3 PLC Code UL 746A
Arc Resistance, Tungsten {PLC}   6 PLC Code ASTM D 495
Injection Molding        
Drying Temperature   110-120 °C  
Drying Time   3-4 hrs  
Drying Time (Cumulative)   8 hrs  
Maximum Moisture Content   0.02 %  
Melt Temperature   300-325 °C  
Nozzle Temperature   300-325 °C  
Front - Zone 3 Temperature   290-325 °C  
Middle - Zone 2 Temperature   275-320 °C  
Rear - Zone 1 Temperature   265-315 °C  
Mold Temperature   80-110 °C  
Back Pressure   0.3-0.7 MPa  
Screw Speed   20-100 rpm  
Shot to Cylinder Size   30-70 %
想更多的了解PPO(聚苯醚)GFN30/沙伯基础(Noryl)物性表参数,请点击以下PDF文档下载:
PPO(聚苯醚)GFN30/沙伯基础(Noryl)物性表参数
温馨提示:
本物性表参数提供者不承担任何法律责任,建议在选择材料前,就数据值与塑胶材料厂商进行验证。版权归原编辑所有,如有侵权请马上与大家联系.