PC(聚碳酸酯)SLX1432/沙伯基础(SABIC)物性表参数

责任编辑:文和林发表时间:2020-06-19

SABIC(沙伯基础创新塑料)LEXAN PC SLX1432是一种中粘度PC共聚物,增强UV稳定性,添加释放剂,可在不透明的颜色,Typical minimum color tolerance limit is DE CMC < 1.0。
PC(聚碳酸酯)SLX1432/沙伯基础(SABIC)物性表参数PDF文档下载
PC SLX1432
以下是PC(聚碳酸酯)SLX1432/沙伯基础(SABIC)物性表参数
PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
FLAME CHARACTERISTICS 1)      
UL Yellow Card Link   E45329-104199936 - -
UL Recognized, 94HB Flame Class Rating   1.5 mm UL 94
MECHANICAL        
Tensile Stress, yld, Type I, 50 mm/min   65 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min   72 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min   6.1 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min   126 % ASTM D 638
Tensile Modulus, 5 mm/min   2520 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span   105 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span   2490 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min   65 MPa ISO 527
Tensile Stress, break, 50 mm/min   71 MPa ISO 527
Tensile Strain, yield, 50 mm/min   5.8 % ISO 527
Tensile Strain, break, 50 mm/min   123 % ISO 527
Tensile Modulus, 1 mm/min   2590 MPa ISO 527
Flexural Stress, yield, 2 mm/min   99 MPa ISO 178
Flexural Modulus, 2 mm/min   2390 MPa ISO 178
IMPACT        
Izod Impact, notched, 23°C   860 J/m ASTM D 256
Izod Impact, notched, -30°C   123 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C   76 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C   NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C   65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C   10 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm   65 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm   15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm   NB kJ/m² ISO 179/1eU
THERMAL        
Vicat Softening Temp, Rate B/50   137 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed   132 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed   120 °C ASTM D 648
CTE, -40°C to 40°C, flow   6.2E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow   6.2E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow   6.2E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow   6.2E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50   137 °C ISO 306
Vicat Softening Temp, Rate B/120   140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm   118 °C ISO 75/Af
Relative Temp Index, Elec 1) 80 °C UL 746B
Relative Temp Index, Mech w/impact 1) 80 °C UL 746B
Relative Temp Index, Mech w/o impact 1) 89 °C UL 746B
PHYSICAL        
Specific Gravity   1.22 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm   0.6-0.8 % SABIC method
Melt Flow Rate, 300°C/1.2 kgf   10 g/10 min ASTM D 1238
Density   1.23 g/cm³ ISO 1183
Water Absorption, (23°C/saturated)   0.3 % ISO 62-1
Moisture Absorption (23°C / 50% RH)   0.1 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg   9 cm³/10 min ISO 1133
Injection Molding        
Drying Temperature   120 °C  
Drying Time   3-4 hrs  
Drying Time (Cumulative)   48 hrs  
Maximum Moisture Content   0.02 %  
Melt Temperature   295-315 °C  
Nozzle Temperature   290-310 °C  
Front - Zone 3 Temperature   295-315 °C  
Middle - Zone 2 Temperature   280-305 °C  
Rear - Zone 1 Temperature   270-295 °C  
Mold Temperature   70-95 °C  
Back Pressure   0.3-0.7 MPa  
Screw Speed   40-70 rpm  
Shot to Cylinder Size   40-60 %  
Vent Depth   0.025-0.076 mm