沙伯基础SABIC塑料LEXAN 3413R聚碳酸酯(PC)是一种可注射成型的阻燃级产品,填充30%玻璃纤维, 它具有UL94 V1 @ 2mm等级,并提供各种不透明颜色选项。
沙伯基础SABIC塑料LEXAN 3413R PC物性表参数PDF文档下载
LEXAN 3413R
以下是LEXAN(沙伯基础)3413R/PC(聚碳酸酯)物性表参数
PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
MECHANICAL        
Taber Abrasion, CS-17, 1 kg   24 mg/1000cy SABIC method
Tensile Stress, break, 5 mm/min   100 MPa ISO 527
Tensile Strain, break, 5 mm/min   2 % ISO 527
Tensile Modulus, 1 mm/min   9000 MPa ISO 527
Flexural Stress, break, 2 mm/min   130 MPa ISO 178
Flexural Modulus, 2 mm/min   7000 MPa ISO 178
IMPACT        
Izod Impact, unnotched 80*10*3 +23°C   35 kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C   35 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C   7 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C   6 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm   6 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm   5 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm   40 kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm   40 kJ/m² ISO 179/1eU
THERMAL        
Thermal Conductivity   0.22 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow   2.5E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C   PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50   147 °C ISO 306
Vicat Softening Temp, Rate B/120   145 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm   144 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm   139 °C ISO 75/Ae
Relative Temp Index, Elec   130 °C UL 746B
Relative Temp Index, Mech w/impact   125 °C UL 746B
Relative Temp Index, Mech w/o impact   130 °C UL 746B
PHYSICAL        
Mold Shrinkage on Tensile Bar, flow   0.1-0.4 % SABIC method
Density   1.44 g/cm³ ISO 1183
Water Absorption, (23°C/sat)   0.26 % ISO 62
Moisture Absorption (23°C / 50% RH)   0.11 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg   5 cm³/10 min ISO 1133
OPTICAL        
Haze, 2.54 mm   NA % ASTM D 1003
Refractive Index   NA - ISO 489
ELECTRICAL        
Volume Resistivity   >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA   >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm   33 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm   25 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm   16 kV/mm IEC 60243-1
Relative Permittivity, 1 MHz   3 - IEC 60250
Dissipation Factor, 50/60 Hz   0.001 - IEC 60250
Dissipation Factor, 1 MHz   0.01 - IEC 60250
Relative Permittivity, 50/60 Hz   3.1 - IEC 60250
FLAME CHARACTERISTICS        
UL Recognized, 94V-0 Flame Class Rating   1.5 mm UL 94
Glow Wire Flammability Index 850°C, passes at   1 mm IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at   1.6 mm IEC 60695-2-12
Oxygen Index (LOI)   38 % ISO 4589
Injection Molding        
Drying Temperature   120 °C  
Drying Time   2-4 hrs  
Maximum Moisture Content   0.02 %  
Melt Temperature   290-320 °C  
Nozzle Temperature   280-310 °C  
Front - Zone 3 Temperature   290-320 °C  
Middle - Zone 2 Temperature   280-310 °C  
Rear - Zone 1 Temperature   270-300 °C  
Hopper Temperature   60-80 °C  
Mold Temperature   80-120 °C