VALOX(沙伯基础)830/PBT热塑性聚酯/物性表参数

责任编辑:文和林发表时间:2020-04-18

沙伯基础创新塑料SABIC的VALOX 830 PBT是一种加30% GR PBT+ PET,表面光洁度好,典型的应用是热风枪外壳组件、工业胶枪、电器外壳和把手。
沙伯基础创新塑料的VALOX 830 PBT物性表参数PDF文档下载
VALOX 830
以下是VALOX(沙伯基础)830/PBT热塑性聚酯/物性表参数
PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
MECHANICAL        
Tensile Stress, yld, Type I, 5 mm/min   140 MPa ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min   140 MPa ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min   3 % ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min   3 % ASTM D 638
Tensile Modulus, 5 mm/min   10500 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span   205 MPa ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span   205 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span   7400 MPa ASTM D 790
Taber Abrasion, CS-17, 1 kg   30 mg/1000cy SABIC method
Tensile Stress, yield, 5 mm/min   140 MPa ISO 527
Tensile Stress, break, 5 mm/min   140 MPa ISO 527
Tensile Strain, yield, 5 mm/min   3 % ISO 527
Tensile Strain, break, 5 mm/min   3 % ISO 527
Tensile Modulus, 1 mm/min   10500 MPa ISO 527
Flexural Stress, yield, 2 mm/min   215 MPa ISO 178
Flexural Stress, break, 2 mm/min   200 MPa ISO 178
Flexural Strain, break, 2 mm/min   3 % ISO 178
Flexural Modulus, 2 mm/min   8800 MPa ISO 178
Ball Indentation Hardness, H358/30   174 MPa ISO 2039-1
Hardness, Rockwell R   123 - ISO 2039-2
IMPACT        
Charpy Impact, unnotched, 23°C   60 kJ/m² ISO 179/2C
Charpy Impact, unnotched, -30°C   55 kJ/m² ISO 179/2C
Izod Impact, unnotched, 23°C   800 J/m ASTM D 4812
Izod Impact, unnotched, -30°C   800 J/m ASTM D 4812
Izod Impact, notched, 23°C   90 J/m ASTM D 256
Izod Impact, notched, 0°C   90 J/m ASTM D 256
Izod Impact, notched, -30°C   90 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C   3 J ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C   50 kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C   50 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C   10 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 0°C   9 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C   9 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm   9 kJ/m² ISO 179/1eA
Charpy Impact, notched, 23°C   10 kJ/m² ISO 179/2C
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm   9 kJ/m² ISO 179/1eA
Charpy Impact, notched, -30°C   10 kJ/m² ISO 179/2C
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm   60 kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm   50 kJ/m² ISO 179/1eU
THERMAL        
Vicat Softening Temp, Rate A/50   220 °C ASTM D 1525
Vicat Softening Temp, Rate B/50   208 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed   220 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed   200 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed   208 °C ASTM D 648
CTE, -40°C to 40°C, flow   2.7E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow   7.8E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow   1.97E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow   6.59E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, flow   2.5E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow   8.1E-05 1/°C ISO 11359-2
CTE, 23°C to 150°C, flow   1.51E-05 1/°C ISO 11359-2
CTE, 23°C to 150°C, xflow   1.42E-04 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C   PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate A/50   220 °C ISO 306
Vicat Softening Temp, Rate B/50   208 °C ISO 306
Vicat Softening Temp, Rate B/120   208 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm   220 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm   202 °C ISO 75/Ae
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm   220 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm   200 °C ISO 75/Af
Relative Temp Index, Elec   120 °C UL 746B
Relative Temp Index, Mech w/o impact   120 °C UL 746B
PHYSICAL        
Specific Gravity   1.55 - ASTM D 792
Filler Content   30 % ASTM D 229
Mold Shrinkage on Tensile Bar, flow   0.4-0.8 % SABIC method
Mold Shrinkage, flow, 3.2 mm   0.2-1 % SABIC method
Mold Shrinkage on Tensile Bar, xflow   0.6-1 % SABIC method
Melt Flow Rate, 265°C/2.16kgf   16 g/10 min ASTM D 1238
Melt Flow Rate, 265°C/5.0 kgf   45 g/10 min ASTM D 1238
Density   1.55 g/cm³ ISO 1183
Water Absorption, (23°C/sat)   0.15 % ISO 62
Moisture Absorption (23°C / 50% RH)   0.06 % ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg   23 cm³/10 min ISO 1133
Melt Volume Rate, MVR at 265°C/2.16 kg   14 cm³/10 min ISO 1133
Melt Volume Rate, MVR at 265°C/5.0 kg   35 cm³/10 min ISO 1133
Melt Viscosity, 260°C, 1500 sec-1   208 Pa-s ISO 11443
ELECTRICAL        
Volume Resistivity   >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength, in oil, 0.8 mm   27 kV/mm ASTM D 149
Dielectric Strength, in oil, 1.6 mm   23 kV/mm ASTM D 149
Dielectric Strength, in oil, 3.2 mm   15 kV/mm ASTM D 149
Relative Permittivity, 1 MHz   3.2 - ASTM D 150
Dissipation Factor, 1 MHz   0.013 - ASTM D 150
Arc Resistance, Tungsten {PLC}   6 PLC Code ASTM D 495
Hot Wire Ignition {PLC)   0 PLC Code UL 746A
High Voltage Arc Track Rate {PLC}   2 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC}   3 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC}   2 PLC Code UL 746A
Volume Resistivity   >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA   >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm   27 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm   23 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm   15 kV/mm IEC 60243-1
Relative Permittivity, 100 Hz   3.6 - IEC 60250
Relative Permittivity, 1 MHz   3.2 - IEC 60250
Dissipation Factor, 50/60 Hz   0.0008 - IEC 60250
Dissipation Factor, 100 Hz   0.002 - IEC 60250
Dissipation Factor, 1 MHz   0.013 - IEC 60250
Comparative Tracking Index   325 V IEC 60112
Comparative Tracking Index, M   150 V IEC 60112
Relative Permittivity, 50/60 Hz   3.3 - IEC 60250
FLAME CHARACTERISTICS        
UL Recognized, 94HB Flame Class Rating   1.5 mm UL 94
UL Recognized, 94HB Flame Class Rating 2nd value   3 mm UL 94
Glow Wire Flammability Index 750°C, passes at   1 mm IEC 60695-2-12
Injection Molding        
Drying Temperature   110 - 120 °C  
Drying Time   4 - 6 hrs  
Maximum Moisture Content   0.02 %  
Melt Temperature   260 - 285 °C  
Nozzle Temperature   265 - 275 °C  
Front - Zone 3 Temperature   260 - 280 °C  
Middle - Zone 2 Temperature   255 - 280 °C  
Rear - Zone 1 Temperature   240 - 260 °C  
Hopper Temperature   40 - 60 °C  
Mold Temperature   60 - 110 °C

温馨提示:
本物性表参数提供者不承担任何法律责任,建议在选择材料前,就数据值与塑胶材料厂商进行验证。版权归原编辑所有,如有侵权请马上与大家联系.