PA66(尼龙66)AKV35XTS1/德国朗盛/物性表参数

责任编辑:文和林发表时间:2020-04-25

德国朗盛Durethan PA66 AKV35XTS1是一种加35%玻璃纤维p66, 注塑成型,热老化稳定,表面光洁度提高尼龙树脂,根据特定的材料及所需等级,尼龙从环境中吸取潮气的能力也不同。这与增塑剂的效果相同,即可以提高材料的断裂伸长及韧性,但降低了材料的強度和剛度,除了自然色及黑色外,还可以提供一系列的不透明标准颜色;如有需要,也可以提供特定颜色的产品。
PA66 AKV35XTS1
生产商:LANXESS(德国朗盛)、品名:Durethan
PA66(尼龙66)AKV35XTS1/德国朗盛/物性表参数
C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Property Test Condition Unit Standard guide value
  d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.35  
C Molding shrinkage, transverse 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.90  
  Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05  
  Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.15  

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10700 6800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 185 105
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.2 5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 85
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 15
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10 <10
  Izod impact strength   kJ/m² ISO 180-1U 65 70
  Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 15
  Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10 <10
  Flexural modulus 2 mm/min MPa ISO 178-A 10100 6200
  Flexural strength 2 mm/min MPa ISO 178-A 280 180
  Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.5 5
  Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 280 140

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 261  
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 235  
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 250  
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.20  
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.95  

Other properties (23 °C)
C Density   kg/m³ ISO 1183 1410  
  Bulk density   kg/m³ ISO 60 700  

Processing conditions for test specimens
C Injection molding-Melt temperature   °C ISO 294 290  
C Injection molding-Mold temperature   °C ISO 294 80  

Processing recommendations
  Drying temperature dry air dryer   °C - 80  
  Drying time dry air dryer   h - 2-6  
  Residual moisture content   % Acc. to Karl Fischer 0.03-0.12  
  Melt temperature (Tmin - Tmax)   °C - 270-290  
  admissible residence time at Tmax   min - <5  
  Mold temperature   °C - 80-120  
德国朗盛Durethan PA66 AKV35XTS1具有高抗震及抗裂性能,具体指标与材料的等级与含水量有关。弹性体改性的材料即使在低含水量及低温下也具有良好的韧性,硬度高,尤其对于玻纤增強级别产品;拉伸模量:1,300 到 15,700 MPa (取决于含水量),良好的机械性能及阻尼吸声效应、低摩擦力、急速运行能力好,气体阻隔性能好(薄膜级),
密度 1.01~1.23 模具温度 80.0 到 100°C    
加工(熔体)温度 260 到 270°C 注射压力 230 到 250°C    
 
 
预热
 
 
温度/°C
 
 
130°C




 
 
 
注射时间
 
 
20~90
时间/h 4.0hr 高压时间 0~5    
料桶温度/°C 后段 193 到 238°C 冷却时间 20~90  
中段 210 到 249°C 总周期 220 到 260°C    
前段 221 到 254°C 螺杆转数 30 到 60rpm    
喷嘴温度 232 到 274°C 使用注射机类型 螺杆式

温馨提示:
本物性表参数提供者不承担任何法律责任,建议在选择材料前,就数据值与塑胶材料厂商进行验证。版权归原编辑所有,如有侵权请马上与大家联系.